Since the materials used for vacuum contacts are binary and above alloy materials, and the main elements are required to have pseudo alloy characteristics, powder metallurgy and vacuum (controllable atmosphere) melting are adopted in the production and manufacturing process.
Elektrik kontaktlarıİnfiltrasiya üsulu
Infiltration method is a common method to produce refractory metal and low melting point metal pseudoalloy. The high melting point metal powder is pressed and pre sintered (or powder sintered) to form a porous skeleton, and then the low melting point metal is placed above or below the skeleton. At a temperature higher than the melting point of the metal, it melts and infiltrates into the porous skeleton metal to fill the gap, so as to obtain a dense product.
Elektrik kontaktları Qarışıq tozun sinterlənməsi
Toz qarışdırma sinterləmə prosesi adi toz metallurgiyası istehsal prosesidir, yəni toz qarışdırma / presləmə / sinterləmə prosesidir. Keramika və sementlənmiş karbid istehsalında geniş istifadə olunur. Bu, yaxşı işlənmiş metallurgiya üsuludur. Fərqli sinterləmə temperaturuna görə, bərk fazalı sinterləmə və maye fazalı sinterlənməyə bölünə bilər.
Elektrik kontaktları Vakuum qövsünün yenidən əriməsi
Şlaksız və aşağı təzyiqli mühitdə və ya inert atmosferdə, istehlak olunan elektrod DC qövsünün yüksək temperaturu altında sürətlə əriyir və soyuq qəlibdə yenidən bərkiyir, beləliklə ərinti bu yüksək temperaturda ərimə prosesində təmizlənə bilər, beləliklə nail olmaq üçün təmizləmə, strukturu təkmilləşdirmək və performansı yaxşılaşdırmaq məqsədi.